AWS A5.28 ER100S-G Solid wire
TEMO WH70-G, GB/T 39281 G69A4UM21Z
Description:
ER100S-G is a gas shielded solid wire used for high-strength steel with a tensile strength of 690MPa. It adopts rich argon gas protection and its weld metal has excellent comprehensive mechanical properties.
Diameters: Packaging:
0.6mm-4.0mm 1kg, 5kg, 15kg, 250kg,300kg, 350kg
Applications:
Mainly used for welding high-strength steel for important structures of corresponding strength grades. Widely used in fields such as ships, pipelines, engineering machinery, petrochemicals, pressure vessels, bridges, lifting and transportation, high-rise buildings, etc.
Chemical Composition of Deposited Metal (wt.%):
C | Mn | Si | Ni | Mo | S | P | |
AWS | As agreed between supplier and purchaser. | ||||||
GB/T | As agreed between supplier and purchaser. | ||||||
Example value | 0.08 | 1.65 | 0.58 | 0.88 | 0.42 | 0.005 | 0.007 |
Mechanical Properties of Deposited Metal:
Tensile strength /MPa | Yield strength /MPa | Elongation /% | Impact J/℃ | |
AWS | ≥690 | As agreed between supplier and purchaser. | ||
GB/T | 690-890 | ≥600 | ≥14 | ≥47/-40 |
Example value | 725 | 660 | 24 | 89 |
Weld X - ray Flaw Detection: GradeⅠ
Recommended welding parameters:
Diameter /mm | φ1.0 | φ1.2 | φ1.6 | |
Current /A | Flat/horizontal welding | 80-250 | 100-360 | 170-390 |
Notes:
1. Using mixed gas protection, gas code M21 (Ar+(15-25%) CO₂).
2. The dry extension length of the welding wire should be controlled within the range of 15-20mm.
3. Before welding, impurities such as rust, oil stains, and moisture must be removed from the welded parts.
4. After unpacking the wire, attention should be paid to taking moisture-proof measures and using it up as soon as possible.
5. When welding on site, if the wind is too strong, windproof measures should be taken.