AWS A5.22 E308LT1-1 Flux cored wire
TEMO TMF308L, GB/T 17853 TS308L-FC11
Description:
E308LT1-1 is a CO₂ gas shielded flux cored wire for ultra-low carbon stainless steel with titanium slag system. The deposited metal microstructure is austenitic with a moderate amount of ferrite with low crack sensitivity. The deposited metal in the welded state has excellent corrosion resistance and mechanical properties, and excellent resistance to intergranular corrosion. Used for all position welding, with excellent welding process performance, stable arc, and beautiful weld formation.
Diameters: Packaging:
1.2mm, 1.6mm 5kg, 15kg
Applications:
Mainly used for welding ultra-low carbon 18%Cr-8%Ni stainless steel, widely used in fields such as petrochemicals and pressure vessels.
Chemical Composition of Deposited Metal (wt.%):
C | Mn | Si | Ni | S | P | Cr | Mo | Cu | |
AWS | ≤0.04 | 0.5-2.5 | ≤1.0 | 9.0-11.0 | ≤0.030 | ≤0.040 | 18.0-21.0 | ≤0.75 | ≤0.75 |
GB/T | ≤0.04 | 0.5-2.5 | ≤1.0 | 9.0-11.0 | ≤0.030 | ≤0.040 | 18.0-21.0 | ≤0.75 | ≤0.75 |
Example value | 0.035 | 1.60 | 0.60 | 9.5 | 0.015 | 0.020 | 19.2 | 0.24 | 0.02 |
Mechanical Properties of Deposited Metal:
Tensile strength /MPa | Elongation /% | |
AWS | ≥520 | ≥30 |
GB/T | ≥520 | ≥25 |
Example value | 580 | 46 |
Weld X - ray Flaw Detection: Grade Ⅱ
Recommended welding parameters(DC﹢):
Diameter /mm | φ1.2 | φ1.6 |
Current /A | 120-220 | 180-300 |
Voltage /V | 20-32 | 20-32 |
Gas flow(L/min) | 20-25 | 20-25 |
Notes:
1. Using CO₂ gas protection, the purity of CO₂ gas is above 99.8%.
2. The dry extension length of the welding wire should be controlled within the range of 15-25mm.
3. Before welding, impurities such as rust, oil stains, and moisture must be removed from the welded parts.
4. After unpacking the wire, attention should be paid to taking moisture-proof measures and using it up as soon as possible.
5. When welding on site, if the wind is too strong, windproof measures should be taken.
6. Preheating and inter passage temperature≤80℃.